Technology

About Glass Lining

Types of Glass Offered:-

We have variety of glass to meet your varying process needs.

The array of glass that we have are as under:

1) Standard Cobalt Blue Glass (TE 9200)

2) High Temperature Green Glass (TE 9400G)

3) White Glass (TE 9300W)

4) Pharma Glass (TE 9500P)

Glass Testing Standard:-

STANDARD	LIQUID PHASE		VAPOUR PHASE

DIN – 51157 Hydrochloric Acid	0.01 mm/year		0.04 mm/year
DIN – 51156 Sodium Hydroxide	0.21 mm/year		-----
DIN – 51156 Water	0.008 mm/year		0.013 mm/year
DIN – 51167	Temperature of failure 260⁰C Statiflux surface cracks		-----
Abrasion Porcelain Enamel Institute, Ohio, USA	3.5 mg/min		-----

Impact Test carried out at		40 NM

Coating Thickness	1.0 to 2.2 mm	Modulus of Elasticity	75000 N/mm²
Specific Weight	2.5 G/cm³	Elongation	0.1 %
Tensile Strength	70 N /mm²	Abrasion	3.5 mg/min
Compressive Strength	800 N/mm²	Flexibility	Lined glass bends with the base metal until latter reaches permanent deformation
Hardness HV	700 Kg/mm²	Chipping Tendency	None, under normal conditions
Coefficient of Thermal Conductivity	1.2 W/MK	Chemical Resistance	Highly resistance to almost all substances. Insensitive to the action of oxidizing or reducing agents. No catalytic effect. No product contamination.
Specific Heat	0.82 KJ/Kg K	Structural	Dielectric in nature, hence no electrochemical corrosion. It does not age as it is amorphous in structure.
Electric Resistivity	10¹³ ?/cm at Ambient Temperature	Surface	Exceptionally smooth, hence easier to clean, excellent resistance to wear, impermeable to gases, prevent sticking and the growth of micro flora, biologically easily sterilizable.
Dielectric Strength	20-30 KV/mm	Surface